Bifunctional TiO2 underlayer for α-Fe2O3 nanorod based photoelectrochemical cells: Enhanced interface and Ti4+ doping

Cited 1 times inthomson ciCited 2 times inthomson ci
Title
Bifunctional TiO2 underlayer for α-Fe2O3 nanorod based photoelectrochemical cells: Enhanced interface and Ti4+ doping
Author
Annamalai, AlaqappanShinde, Pravin S.Subramanian, ArunprabaharanKim, Jae YoungKim, Jin HyunChoi, Sun HeeLee, Jae SungJang, Jum Suk
Issue Date
2015-03
Publisher
ROYAL SOC CHEMISTRYROYAL SOC CHEMISTRY
Citation
JOURNAL OF MATERIALS CHEMISTRY A, v.3, no.9, pp.5007 - 5013
Abstract
A thin, compact TiO2 underlayer for hematite-based photoelectrochemical cells was prepared by simple spin coating and showed a dramatic increase in device performance and photocurrent density. The introduction of TiO2 underlayers induced a noticeable change in the nanostructure. In contrast to the conventional strategies based on underlayers, the compact TiO2 underlayers can act as both a charge recombination barrier and also as a source for titanium dopants. One could simply take advantage of fortuitous doping of Sn from FTO into hematite lattice during the activation step, and is converted into intentional doping of Ti4+ from the TiO2 underlayer into the hematite lattice. Ti4+ doping in hematite lattice is highly probable during the sintering of FTO/TiO2/α-Fe2O3 photoanodes at 800 °C, which has been confirmed by XPS measurements. Based on electrochemical studies, it is evident that the TiO2 underlayer effectively suppresses charge recombination at the FTO/α-Fe2O3 interface and provides possible Ti4+ doping apart from Sn diffusion from FTO substrates when sintered at high temperature (800°C). In contrast, only charge recombination was suppressed at lower sintering temperature (550°C). This is the first report on the elemental doping of Ti4+ from the TiO2 underlayer when sintered at high temperature
URI
https://scholarworks.unist.ac.kr/handle/201301/10922
URL
http://pubs.rsc.org/en/Content/ArticleLanding/2015/TA/C4TA06315E#!divAbstract
DOI
10.1039/c4ta06315e
ISSN
2050-7488
Appears in Collections:
ECHE_Journal Papers
Files in This Item:
There are no files associated with this item.

find_unist can give you direct access to the published full text of this article. (UNISTARs only)

Show full item record

qrcode

  • mendeley

    citeulike

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

MENU