Separation of CO2 by Modified g-Al2O3 Membranes

Cited 0 times inthomson ciCited 0 times inthomson ci
Title
Separation of CO2 by Modified g-Al2O3 Membranes
Other Titles
이산화탄소 분리용 복합 알루미나 막의 제조
Author
Lee, Kun-HongCho, Yoon-KyoungHan, Kunwoo
Issue Date
1995
Publisher
한국화학공학회
Citation
Journal of the Korean Institute of Chemical Engineers, v.33, no.5, pp.570 - 579
Abstract
솔-젤법에 의하여 코팅용 솔을 만들고, 이 솔을 이용하여 알루미나 복합막을 제조하였다. AlOOH솔은 Yoldas법에 의하여 준비하였으며, HCl/알콕사이드 몰비가 0.07인 솔이 가장 투명하고 입자의 크기도 최소였다. 이 솔은 비지지 Υ-알루미나 막의 제조에서 최대의 표면적을 나타내었다. ALOOH 솔을 지지체에 코팅-건조-열처리를 반복하여 기공이 큰 α-알루미나 위에 기공이 작은 γ-알루미나 층을 형성하였다. 침적코팅, 진공코팅 및 펌프코틴의 3가지 코팅법을 시도하였으며, 0.8M의 솔로 3회아상 코팅-건조-열처리하는 것이 필요하였다. 코팅-건조를 반복한 후 최종적으로 열처리하거나, 너무 진한 솔을 사용할 경우에는 균열이 생기거나 코팅층이 벗겨지기 쉬웠다. 실리카나 CaO 용액을 사용하여 알루미나 복합막의 표면을 개지할 수 있었다. 사용하는 용액에 따라서 도판트의 분포를 조절할 수 있었다. Alumina composite membranes were manufactured using coating sols witch were synthesized through sol-gel method. The AlOOH sol, prepared with the Yoldas Method, appeared the most transparent and contained the smallest. Particles when the HCl/alkoxide molar ratio was 0.07. The same sol resulted in the unsupported γ-alumina membrane with the largest surface area. γ-Alumina layers with small pores were formed on top of the -alumina supports with larger pores by repeating the coating-drying-calcining cycle with AlOOH sols. Dip coating, vacuum coating and pump coating methods were applied and at least 3 coating-drying-calcining cycles were necessary with 0.8 M sols. Crack formation or peeling of coating layers were frequently observed when repeated coating-drying cycles were followed by final calcining or concentrated sols were used. Surfaces of alumina composite membranes could be modified with silica or CaO. Distribution of dopant could be controlled by changing the solutions.
URI
https://scholarworks.unist.ac.kr/handle/201301/9118
ISSN
0304-128X
Appears in Collections:
BME_Journal Papers
Files in This Item:
There are no files associated with this item.

find_unist can give you direct access to the published full text of this article. (UNISTARs only)

Show full item record

qrcode

  • mendeley

    citeulike

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

MENU