Thin aluminum oxide (Al2O3) films were grown by plasma-assisted atomic layer controlled deposition (PAALD) method using Dimethylethylamine alane ((CH3)(2) (C2H5)N:AlH3) (DMEAA). Al was deposited by PAALD method, then the Al films were oxidized into Al2O3 by the plasma oxidation in the same chamber without breaking the vacuum. Al2O3 thin films of 15 mn thickness were prepared by repetition of the above mentioned process. Thus, prepared Al2O3 thin films showed a refractive index of 1.68. The thickness and the refractive index fluctuation of the film over a 4-in. wafer were +/-2.3% and +/-1.9%, respectively, for atomic layer controlled deposited films. The leakage current density and breakdown field were measured to be about 10(-8) A/cm(2) at 1 and 7 MV/cm, respectively. (C) 2001 Published by Elsevier Science B.V.