가교된 Epoxy Resin 분산 액정의 제조 및 상분리 거동

Cited 0 times inthomson ciCited 0 times inthomson ci
Title
가교된 Epoxy Resin 분산 액정의 제조 및 상분리 거동
Other Titles
Synthesis of Crosslinked Liquid Crystalline Epoxy Polymer and LMWLC Phase Separation Behavior
Author
Park, Lee SoonAhn, WonsoolKum, Chang Dae
Keywords
polymer dispersed liquid crystal(PDLC); polymerization induced phase separetion(PIPS); epoxy based liquid crystalline polymer
Issue Date
1997-05
Publisher
POLYMER SOC KOREA
Citation
POLYMER-KOREA, v.21, no.1, pp.26 - 35
Abstract
말단에 NH2기를 가지는 저분자 액정 4-[4-(n-aminoalkyloxy) phenylazo]benzonitrile AAB (n=6, 8)을 합성하였으며 DSC 및 편광 현미경 관찰을 통해 nematic texture를 확인하였다. AAB(6)과 ethyleneglycol diglycidyl ether (EGDE)를 반응시켜 선형 epoxy계 측쇄 액정 고분자(ELCP)를 얻었으며 액정 전이온도(Tiso)는 저분자 액정, AAB(6)보다 낮게 나타났다. AAB(n=6, 8)과 EGDE 및 가교제로서 1,10-diaminodecane (DA) 및 triglycidyl isocyanurate (TGI)를 이용하여 각각 가교된 epoxy계 액정 중합체 XDLCP 및 XTLCP를 얻었으나 가교 효율은 낮게 나타났다. XTLCP의 경우 TGI 함량이 30mo1% 이상에서 액정성을 나타내지 않았다. 상용품 저분자 액정 (E7)을 EGDE/DA 단량체와 혼합하여 polymerization induced phase separation 법으로 가교 고분자 분산액정을 제조하였으며 E7의 무게 비율이 35wt% 이상에서 저분자 액정의 상분리가 관찰되었다. 분산상의 전이온도는 저분자 액정 E7의 TNI=60.5와 유사하게 나타났다.
URI
Go to Link
ISSN
0379-153X
Appears in Collections:
MSE_Journal Papers
Files in This Item:
가교된_Epoxy_Resin_분산_액정의_제조_및_상분리_거동.pdf Download

find_unist can give you direct access to the published full text of this article. (UNISTARs only)

Show full item record

qrcode

  • mendeley

    citeulike

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

MENU